Influence of Epoxy Resin Emulsion Without Curing A…
Author:YAN Peiyu1  YUE Lei1  DAI Dan2  LUO Yuwei2 
Unit:1. Department of Civil Engineering  Tsinghua University  Beijing 100084  China  2. China Oilfield Services Limited  Yanjiao 065201  Hebei  China 
Keyword:epoxy resin emulsion  cement paste  hydration process 
Year,volume(Issue):page number:2017,45(5):608-613

 Epoxy resin modified cement pastes containing different percentages of emulsion were prepared using two kinds of epoxy resin emulsions with different polymerization degrees. The influence of epoxy resin emulsion without curing agent on the early hydration process of oil well cement pastes was investigated at different temperatures using isothermal hydration heat evolution, scanning electron microscopy and X-ray diffraction. The results show that the hydration process of epoxy resin modified cement pastes is delayed, compared to that of blank cement pastes, while their hydration products are similar. There is an epoxy resin film wrapping the particles in hardened cement pastes, which can fill the capillary pores of cement stones. Hence, the compressive strength of cement stones increases slightly as the content of epoxy resin emulsion increases.

Foundation item:
国家自然科学基金项目(No. 51678344,No. 51678343)。
About The Author:

 [1]Syed T, Cutler T. Well Integrity Technical and Regulatory Considerations for CO2 Injection Wells[C]//SPE International Conference on Health, Safety and Environment in Oil and Gas Exploration and Production[C]. Society of Petroleum Engineers, 2010.

[2]Detroit W J, Sanford M E, Chatterji J, et al. Oil well cementing process[P]. US, USRE31190, 1983.
[3]李铭. 聚合物改性水泥基材料研究[D]. 武汉工程大学, 2012.
LI Ming. The modification of cement by polymer material (dissertation, in Chinese). Wuhan Institute of Technology, 2012.
[4]方萍. 丙苯乳液改性聚合物水泥力学性能和内部结构研究[J]. 混凝土, 2001(3): 46–48.
FANG Ping. Concrete (in Chinese), 2001(3): 46–48.
[5]陈友治, 李方贤, 王红喜. 水乳环氧对水泥砂浆强度的影响[J]. 重庆大学学报: 自然科学版, 2003, 26(12): 48–50.
CHEN Youzhi, LI Fangxian, WANG Hongxi. J Chongqing Univ: Sci Technol (in Chinese), 2003, 26(12): 48–50.
[6]沈凡, 黄绍龙, 孙政, 等. 水性环氧树脂-水泥-乳化沥青复合胶结体系的硬化机理[J]. 中南大学学报: 自然科学版, 2012, 43(1): 105–110.
SHEN Fan, HUANG Shaolong, SUN Zheng, et al. J Central South Univ: Sci Technol, 2012, 43(1): 105–110.
[7]OTA M, OHKUBO T, OCHI M, OHAMA Y. Strength development through long-term dry curing of initially combind wet/dry-cured and steam-cured hardener-free epoxy-modified mortars[J]. J Struct Construct Eng (in Japanese), 2011, 76(663): 875–880.
[8]Ariffin N F, Hussin M W, Sam A R M, et al. Strength properties and molecular composition of epoxy-modified mortars[J]. Construct Build Mater, 2015, 94: 315–322.
Service and feedback:
Article download】【Add to Wishlist
Editorial Department of Journal of the Chinese Ceramic Society
Address: No.11 Sanlihe Road, Beijing, China    P.C.:100831