柠檬酸对氯氧镁水泥的改性

单位：(1. 辽宁科技大学高温材料与镁资源工程学院辽宁鞍山 114000 2. 大连理工大学建设工程学部辽宁大连 116024 3. 南京航空航天大学土木工程系南京 210016)

分类号：TQ172

出版年,卷(期):页码：2019,47(7):0-0

DOI：

摘要：

为了拓宽氯氧镁水泥(MOC)在建筑、道路等行业的应用，向MOC中掺入柠檬酸，分析了柠檬酸对MOC抗压强度、耐硫酸盐侵蚀性、耐水性、相组成、热稳定性、凝结时间和微观形貌的影响。结果表明：MOC中掺入柠檬酸提高了水化产物5相含量和耐水性；降低了MOC的抗压强度、热稳定性及总孔隙率；延长了MOC的凝结时间。此外，掺入柠檬酸的MOC浸泡在硫酸钠溶液28 d后提高了MOC的耐水性，MOC强度保留系数达到0.8。

Citric acid was added into magnesium oxychloride cement (MOC) to expand the application of MOC in building and road industry. The effect of citric acid on the compressive strength, sulfate corrosion resistance, water resistance, composition, thermal stability, setting time and microstructure of MOC was investigated. The results show that adding citric acid can increase the content of phase 5Mg(OH)2•MgCl2•8H2O and improve the water resistance of MOC. Adding citric acid leads to a reduction in compressive strength, thermal stability and total porosity, and prolongs the setting time of MOC. In addition, soaking in sulfate solution after 28 d can improve the sulfate corrosion resistance and the compressive strength retention coefficient of MOC with citric acid (i.e., 0.8).

基金项目：

国家自然科学基金面上项目(51778101)

作者简介：

参考文献：

[1] LI Z J, CHAU C K. Influence of molar ratios on properties of magnesium oxychloride cement[J]. Cem Concr Res, 2007, 37(6): 866?870.

[2] DEMEDIUK T, COLE W F, HUEBER H V. Studies on magnesium and calcium oxychlorides[J]. Aust J Chem, 1955, 8(2): 215?233.

[3] LI Y, LI Z J, Pei H F, et al. The influence of FeSO4 and KH2PO4 on the performance of magnesium oxychloride cement[J]. Constr Build Mater, 2016, 102: 233?238.

[4] TAN Y N, LIU Y, GROVER L. Effect of Tartaric acid on the properties of magnesium oxychloride cement as a biomaterial[J]. Cem Concr Res, 2014, 56(2): 69?74.

[5] LU Z Y, ZHANG J R, SUN G X, et al. Effects of the form-stable expanded perlite/paraffin composite on cement manufactured by extrusion technique[J]. Energy, 2015, 82: 43?53.

[6] WANG N, YU H F, BI W L, et al. Effects of sodium citrate and phosphoric acid on the properties of magnesium oxysulfate cement[J]. Constr Build Mater, 2018, 169: 697?704.

[7] 李颖, 余红发, 董金美, 等. MOC的水化产物、相转变规律和抗水性评价方法的研究进展[J]. 硅酸盐学报, 2013, 41(11): 1465?1473.

LI Ying, YU Hongfa, DONG Jinmei, et al. J Chin Ceram Soc, 2013, 41(11): 1465?1473.

[8] 余红发. MOC及其应用[M]. 北京: 中国建材工业出版社, 1993: 219?220.

[9] CHAU C K, CHAN J, LI Z J. Influence of fly ash on magnesium oxychloride mortar[J]. Cem Concr Comp, 2009, 31: 250?254.

[10] DENG D H, ZHANG C M. The formation mechanism of the hydrate phases in magnesium oxychloride cement[J]. Cem Concr Res, 1999, 29(9): 1365?1371.

[11] GUALTIERI A F. Accuracy of XRPD QTA using the combined Rietveld-RIR method[J]. J Appl Crystallogr, 2000, 33(2): 267?278.

[12] 张传镁, 邓德华. MOC耐水性及其改善的研究[J]. 硅酸盐学报, 1995, 23(6): 673–679.

ZHANG Chuamei, DENG Dehua. J Chin Ceram Soc, 1995, 23(6): 673–679.

[13] WU C Y, YU H F, DONG J M, et al. Effects of material ration, fly ash, and phosphoric acid on magnesium oxysulfate cement[J]. ACI Mater J, 2014, 111(3): 291?297.

[14] WU C Y, CHEN W H, ZHANG H F, et al. The hydration mechaninsm and performance of modified magnesium oxysulfate cement by tartaric acid[J]. Constr Build Mater, 2017, 144: 516?524.

[15] 文静. MOC的水化历程及动力学机理研究[D]. 北京: 中国科学院大学, 2013.

WEN Jing. Study on hydration mechanism and kinetic of magnesium oxychloride cement (in Chinese, dissertation). Beijing: University of Chinese Academy of Science, 2013.

[16] DINNEBIER R E, HALASZ I, FREYER D, et al. The crystal structures of two anhydrous magnesium hydroxychloride phases from in situ synchrotron powder diffraction data[J]. Z Anorg Allg Chem, 2011, 637(11): 1458?1462.

[17] 崔崇, 马保国, 崔可浩, 等. MOC水化机理与水化动力学研究[J]. 武汉工业大学学报, 1994, 16(2): 37?41.

CUI Chong, MA Baoguo, CUI Kehao, et al. J Wuhan Univ Tech (in Chinese), 1994, 16(2): 37?41.

[18] 王佩玲, 余樑, 冯玲英, 等. 水化产物的结晶形态变化对氯镁水泥抗水性能的影响[J]. 无机材料学报, 1991, 6(3): 343–350.

WANG Peiling, YU Liang, FENG LinYing, et al. J Inorg Mater(in Chinese), 1991, 6(3): 343–350.

[19] CASTRO R H R, TORRES R B, PEREIRA G J, et al. Interface energy measurement of MgO and ZnO: understanding the thermodynamic stability of nanocarticles[J]. Chem Mater, 2010, 22(8): 2502?2509.

[20] 赵华, 王永维, 关博文, 等. 粉煤灰对MOC早期性能的影响[J]. 材料导报, 2015, 29(9): 117?121.

ZHAO Hua, WANG Yongwei, GUAN Bowen, et al. Mater Rev (in Chinese), 2015, 29(9): 117?121.

[21] 余学飞. 苛性白云石制备MOC水化机理的研究[J]. 硅酸盐学报, 1998, 26(4): 527?531.

YU Xuefei. J Chin Ceram Soc, 1998, 26(4): 527?531.

服务与反馈：

【文章下载】【加入收藏】